Index / Products / Stainless Steel Welding / Alloy Wire / Alloy wires for high-temperature mechanical applications

Stainless Steel Welding / Alloy Wire / Alloy wires for high-temperature mechanical applications

INACREEP 600

Nominal Composition:
• Ni 72 min
• Cr 14,0-17,0
• Fe 6,0-10,0
• Mn 1,0 max
• Si 0,5 max
• Cu 0,5 max
• C 0,08 max 6

Material Characteristics:

- Specific resist. at 20 °C 100 micro ohm/cm
- Density 8,55 g/cm3
- Approx. Melting Point 1400 °C

Reference norms:
- ASTM B166 UNS N06600
- DIN 17742 - NiCr15Fe - Wst 2.4816
- EN 10095-99 NiCr15Fe - Wst 2.4816

INACREEP 601

Nominal Composition:
• Ni 58,0-63,0
• Cr 21,0-25,0
• Al 1,0-1,7
• Mn 1,0 max
• Si 0,5 max
• Cu 1,0 max
• C 0,1 max • Fe rem.

Material Characteristics:

- Specific resist. at 20 °C 121 micro ohm/cm
- Density 8,06 g/cm3
- Approx. Melting Point 1350 °C

Reference norms:
- ASTM B166 UNS N06601
- DIN 17742 NICR23FE Wst 2.4851
- EN 10095-99 NiCr23Fe - Wst 2.4851

INACREEP DS

Nominal Composition:
• Ni 35,0-39,0
• Cr 17,0-19,0
• Si 1,5-2,5
• Mn 0,8-1,5
• C 0,10 max
• Fe rim.

Material Characteristics:

- Specific resist. at 20 °C 105 micro ohm/cm
- Density 7,95 g/cm3
- Approx. Melting Point 1380 °C

Reference norms:
- BS 3075 NA17

INACREEP 40 Cb

Nominal Composition:
• Ni 34,0-36,0
• Cr 21,0-22,0
• Si 1,75-2,25
• Cb 1,0-2,0
• Mn 0,58 max
• C 0,08 max
• Fe rem.

Material Characteristics:

- Specific resist. at 20 °C 105 micro ohm/cm
- Density 7,95 g/cm3
- Approx. Melting Point 1380 °C

Reference norms:
- EN 10095-99 X10NiCrSiNb 35-22 - Wst 1.4887

INACREEP 625

Nominal Composition:
• Ni 58,0 min
• Cr 20,0-23,0
• Mo 8,0-10,0
• Fe 5,0 max
• Cb 3,15-4,15

• Mn 0,5 max
• Si 0,5 max

Material Characteristics:

- Specific resist. at 20 °C 127 micro ohm/cm
- Density 8,44 g/cm3
- Approx. Melting Point 1320 °C

Reference norms:
- AWS A5.14 (ERNiCrMo3)
- BS 2901 PT5: NA43

INACREEP 800H

Nominal Composition:
• Ni 30,0-34,0
• Cr 19,0-23,0
• Mn 1,5 max
• Si 1,0 max
• Cu 0,75 max
• Ti 0,15-0,60
• C 0,06-0,10
• Fe rim.

Material Characteristics:

- Specific resist. at 20 °C 104 micro ohm/cm
- Density 7,94 g/cm3
- Approx. Melting Point 1410 °C

Reference norms:
- ASTM B408 UNS N08811
- EN 10095-99 X10NiCrAlTi 32-21 - Wst 1.4876